Barrier design facilitates ingress of jointing compound in joint
Crimp from centre mark outwards - clearly marked crimping lines
Crimp with standard Australian/NZ hex dies
Minimised casting imperfections in the metal
Aluminium Link - Barrier Type
For stranded sector and circular stranded aluminium conductor.
Aluminium links are manufactured from solid 99.6% pure electrical grade aluminium rod. The forging process during rod manufacture eliminates any imperfections in the metal structure. This improves the long-term electrical reliability, eliminating future hot joints. The links are a barrier type, mainly because this forces jointing compound back along the conductor strands during crimping, and also to act as a barrier link with oil filled cables etc. These links also have a unique 'funnel' entry, which means that stranded sector cable can be easily inserted into the barrel.
The barrels are chemically treated to reduce contact resistance, and they are filled with jointing compound and capped. Before crimping, the conductors should be scratch brushed. The links should be crimped with standard hexagonal dies, crimping from the centre outwards to force jointing compound into the conductors.
The standard metric range is available, however we can manufacture any special format or imperial link on request.
Aluminium Link - Barrier Type Features
Manufactured from solid 99.6% pure electrical grade aluminium rod
Forging process during rod manufacture eliminates any imperfections in the metal structure
Unique 'Funnel Entry' design
Standards and Compliance
AS/NZS4325 Part 1; IEC France; DIN/VDE Germany; JIS Japan; BS United Kingdom; UL/NEMA USA.
Nominal Conductor (mm2): 800
Aluminium 99.6% pure
Tensile Strength 110 MPa
Ductile Strength 28%
Final Metal State Fully Annealed
-20 to +140 deg C
Resistivity 2.6 micro-ohm cm (max)
Conductivity 61.8% IACS (min)
|Cable Size (mm2):||800|
|Lugs and Links - Material:||Aluminium|